周恺,谢发勤,吴向清,王少青,李国平.TC21钛合金微弧氧化涂层微动磨损行为研究[J].稀有金属材料与工程(英文),2021,50(8):2831~2840.[Zhou Kai,Xie Faqin,Wu Xiangqing,Wang Shaoqing and Li Guoping.Fretting wear damage mechanism of plasma electrolytic oxidation coatings on TC21 titanium alloy[J].Rare Metal Materials and Engineering,2021,50(8):2831~2840.]
Fretting wear damage mechanism of plasma electrolytic oxidation coatings on TC21 titanium alloy
Download Pdf  View/Add Comment  Download reader
Received:March 22, 2021  
DOI:
Key words: TC21 titanium alloy  plasma electrolytic oxidation  fretting wear  damage mechanism
Foundation item:陕西省自然科学基础研究计划(项目号2021JM-055),国家自然科学基金资助(项目号52001256)
Author NameAffiliation
Zhou Kai,Xie Faqin,Wu Xiangqing,Wang Shaoqing and Li Guoping  
Hits: 22
Download times: 0
Abstract:
      The effects of normal load (60 N, 40 N and 20 N) on the tangential fretting wear properties of the TC21 titanium alloy and plasma electrolytic oxidation (PEO) coatings were investigated under displacement amplitudes of 50 μm and 150 μm with a ball-on-plate contact configuration. The results showed that with increase of the displacement amplitude and decrease of the normal load, the fretting wear regime changed from partial slip regime to slip regime. In partial slip regime, the widths of the wear tracks along the fretting direction decreased with the decreasing normal load. Although there was no significant material loss, the extent of micro-cracks initiation and propagation in the micro-slip zone of the TC21 titanium alloy deepened with the decreasing normal load. However, the fretting only played a smooth effect on the PEO coatings. In slip regime, the widths of the wear tracks along the fretting direction increased with the decreasing normal load. There existed local wear in both materials, and the wear degree increased with the increasing amplitude and decreasing normal load. The maximum wear depth of the PEO coatings was shallower than that of the TC21 titanium alloy, which proved that they could improve the fretting wear resistance.