[Zhang Pengjie,Sun Wei,Li Bingshan,Cao Yujie,Tang Dawei,Xu Guangqing,Wei Hanzhong,Xie Guanghuan,Wang Jiquan,Liu Hui,Wang Yongqi,Li Yafeng and Wang Qian.Study on Preparation and Corrosion Behavior of Sintered NdFeB MagnetsCoated with Densed-Ni Coatings[J].Rare Metal Materials and Engineering,2022,51(8):2863~2869.]
Study on Preparation and Corrosion Behavior of Sintered NdFeB MagnetsCoated with Densed-Ni Coatings
Download Pdf  View/Add Comment  Download reader
Received:August 24, 2021  Revised:October 08, 2021
DOI:
Key words: Sintered NdFeB  Densed-Ni coatings  Vickers hardness  Corrosion behavior
Foundation item:国家自然科学基金资助(项目号××××)
Author NameAffiliation
Zhang Pengjie,Sun Wei,Li Bingshan,Cao Yujie,Tang Dawei,Xu Guangqing,Wei Hanzhong,Xie Guanghuan,Wang Jiquan,Liu Hui,Wang Yongqi,Li Yafeng and Wang Qian  
Hits: 27
Download times: 43
Abstract:
      The densed-Ni coatings on sintered NdFeB magnets was prepared by high-energy ball milling method, and the densed-Ni coating was tested by film/substrate bonding force and Vickers hardness. The corrosion resistance of the magnets was studied by neutral salt spray test and high temperature PCT test. The corrosion process of the magnets was further analyzed by static full immersion test. The results showed that the Ni coating on the magnet surface could be densified by ball milling process. The microhardness of Ni-D24/NdFeB magnet increased from 427.95 HV to 502.67 HV and the binding force increased from 16.30 Mpa to 23.85 Mpa at 400 rpm and 24 h ball milling time, which indicated better mechanical damage resistance. The self-corrosion current density of the coating reduced by one order of magnitude compared with that of Ni/NdFeB magnet, and the resistance time to neutral salt spray increased from 312 h to 480 h, showing better corrosion resistance.