Formability of Ni/Al micro-laminated composite sheet
Author:
Affiliation:

1.School of materials science and engineering,Taiyuan University of Technology;2.Advanced Metal Composite Material Forming Technology and Equipment Engineering Research Center of Ministry of Education

Clc Number:

TG111.91;TG146.1;TG113.2

Fund Project:

The National Natural Science Foundation of China (General Program, Key Program, Major Research Plan)

  • Article
  • |
  • Figures
  • |
  • Metrics
  • |
  • Reference
  • |
  • Related
  • |
  • Cited by
  • |
  • Materials
  • |
  • Comments
    Abstract:

    The Ni/Al micro-laminated composite sheet was prepared by the vacuum hot pressing method. The mechanical properties and crack initiation and propagation laws of Ni/Al micro-laminated composite sheet were studied through uniaxial tensile experiments under different temperatures and different deformations degree. The results show that the Ni/Al micro-laminated composite sheet has poor plasticity from room temperature to 400°C, and when the deformation is only 5%, the NiAl3 and Ni2Al3 intermetallic compound layer has produced more cracks perpendicular to the tensile direction. The Ni/Al micro-laminated composite sheet exhibits good plastic deformation ability at 600℃, with the elongation at break as high as 56%, and when the deformation reaches 20%, the NiAl3 layer begins to appear microcracks, and the crack does not propagate to Ni2Al3 layer and Al layer when the deformation reaches 50%. The pressure free bulging experiment was used to study the forming performance of the Ni/Al micro-laminated composite sheet at 600℃, and the microstructure distribution of the bulging part was characterized. The results show that the limit bulging rate (limit bulging height/die diameter) of Ni/Al micro-laminated composite sheet at 600℃/5.5MPa/8min can reach 36.7%. The wall thickness of the gas bulged spherical shell gradually decreases from the bottom to the top, the top Ni and Al layers were severely necked, and cracks occurred in the NiAl3 layer, but they did not extend to the Ni2Al3 layer and the Al layer.

    Reference
    Related
    Cited by
Get Citation

[Gong Pengtao, Lin Peng, Meng Lingjian, Huang Zhongsen, Cao Xiaoqing, Wang Tao. Formability of Ni/Al micro-laminated composite sheet[J]. Rare Metal Materials and Engineering,2022,51(11):4258~4264.]
DOI:10.12442/j. issn.1002-185X.20210913

Copy
Article Metrics
  • Abstract:
  • PDF:
  • HTML:
  • Cited by:
History
  • Received:October 20,2021
  • Revised:November 17,2021
  • Adopted:January 05,2022
  • Online: December 02,2022
  • Published: November 30,2022