Effect of ultrasonic power on the organization and performance of 7075 aluminum alloy CMT welding joint
Author:
Affiliation:

Clc Number:

Fund Project:

  • Article
  • |
  • Figures
  • |
  • Metrics
  • |
  • Reference
  • |
  • Related
  • |
  • Cited by
  • |
  • Materials
  • |
  • Comments
    Abstract:

    In order to solve the problems of large stomata, coarse grain and poor mechanical properties of the aluminum alloy joints, the welding of the 7075 aluminum alloy thin sheet was completed by using the CMT welding method, and the ultrasonic wave was introduced in the welding process.The influence of different ultrasonic power on welded joint stomata, microstructure and mechanical properties were investigated by gold phase,EBSD,and mechanical properties.The results show that ultrasonic vibration can significantly reduce the number of stomata and increase the melting width, and the width of HAZ decreases with the microhardness of welding joints at 1200W by about 8.93HV, tensile strength 5by about 85MPa and fracture elongation by 1.4%.According to EBSD results, the average grain size of the weld was 36.89 μm when the ultrasonic power is 1200W,9.99 μm and the large angle boundary ratio of the welding joint to some extent.

    Reference
    Related
    Cited by
Get Citation

[liruifeng, chenfurong. Effect of ultrasonic power on the organization and performance of 7075 aluminum alloy CMT welding joint[J]. Rare Metal Materials and Engineering,2023,52(1):274~282.]
DOI:10.12442/j. issn.1002-185X.20211105

Copy
Article Metrics
  • Abstract:
  • PDF:
  • HTML:
  • Cited by:
History
  • Received:December 12,2021
  • Revised:March 31,2022
  • Adopted:April 25,2022
  • Online: February 13,2023
  • Published: February 08,2023