| Influence of pre-deformation on aging precipitation and mechanical properties of Cu-Ag alloy |
|
Download Pdf View/Add Comment Download reader |
| Received:April 19, 2022 Revised:August 28, 2022 |
| DOI： |
| Key words: pre-deformation aging precipitation discontinuous precipitation property |
| Foundation item:国家重点研发计划 (项目号：2017YFE0107900),国家111计划2.0(项目号：BP0719037) |
|
| Hits: 112 |
| Download times: 6 |
| Abstract: |
| Cu-Ag alloy is a kind of high-strength and high-conductivity alloy with important application prospects. The improvement of the properties of Cu-Ag alloy depends on the development of the deformation and heat-treatment process. However, the effect of pre-deformation before the heat treatment has not been investigated. The effects of pre-deformation on microstructure and properties after solid solution were investigated using XRD analysis, Vickers hardness, conductivity, metalloscope and scanning electron microscopy. The results show that pre-deformation promotes the recrystallization of Cu-6Ag alloy, and the grain size is obviously reduced. Meanwhile, the pre-deformation reduces the amount of Ag in Cu-6 wt% Ag alloy after aging treatment. Discontinuous precipitates are observed in samples with or without pre-deformation. The discontinuous precipitation in the pre-deformed alloy has a smaller spacing of 95±9.5nm. The hardness in pre-deformation alloy is 85.8 HV lower than that in unpre-deformation alloy. The conductivity of pre-deformed alloy is almost equal to unpre-deformation alloy which is, 90.3%IACS. |
|
|
|