赵晓慧,姚蕾,李天君,张梦霏,潘 伟.等离子放电烧结制备10ScSZ细晶块体及其烧结温度探究[J].稀有金属材料与工程(英文),2020,49(2):500~504.[Zhao Xiaohui,Yao Lei,Li Tianjun,Zhang Mengfei and Pan Wei.Preparation of fine-grained 10ScSZ bulks by Spark Plasma Sintering and Investigation of Sintering Temperature[J].Rare Metal Materials and Engineering,2020,49(2):500~504.]
Preparation of fine-grained 10ScSZ bulks by Spark Plasma Sintering and Investigation of Sintering Temperature
Download Pdf  View/Add Comment  Download reader
Received:April 21, 2019  Revised:May 08, 2019
DOI:
Key words: 10ScSZ  densification  SPS  conductivity
Foundation item:国家自然科学基金(51323001)
Author NameAffiliation
Zhao Xiaohui,Yao Lei,Li Tianjun,Zhang Mengfei and Pan Wei  
Hits: 11
Download times: 0
Abstract:
      Fine-grained compact 10 mol% scandia stabilized zirconia (10ScSZ) bulks were sintered by SPS using powders synthesized by the combustion method as raw materials. The densification process of as-processed powders was investigated by measuring the real-time ram displacement of SPS during heating. It was estimated that the densification temperature of this material was around 1200 ℃ at which the ram displacement is minimum. In order to verify the effectiveness of the approach, 1050 ℃, 1100 ℃, 1150 ℃, 1200 ℃, 1250 ℃ were chosen as the sintered temperature to prepared bulk samples respectively. The results revealed that the 10ScSZ sample sintered at 1150 °C had the highest density, reaching 99.4%, and a fine grain structure with an average grain size of 194 nm, which was basically consistent with the speculated results. In this study, an efficient and reliable method was proposed and confirmed for judging the proper SPS sintering temperature through the densification development.