热处理对TC19钛合金β晶粒尺寸和拉伸性能的影响
Effect of Heat Treatment on β Grain Size and Tensile Property of TC19 Titanium Alloy
摘要
图/表
参考文献
相似文献
本文已被:浏览 29次   下载 0
    
中文摘要: 以TC19钛合金棒材为研究对象,研究了该合金在β相区的晶粒长大特征和机制,并分析了其对拉伸性能的影响规律。结果表明,在975~1 005℃,TC19钛合金的β晶粒长大规律可用Beck方程描述,其在975、990、1 005℃的晶粒长大动力学指数分别为0.517、0.521、0.536。利用Arrhenius公式计算得到TC19钛合金β晶粒长大的表观激活能Q为226.9 kJ/mol。拉伸实验结果表明,TC19钛合金的室温强度对原始β晶粒尺寸不敏感,其断口形貌为典型的准解理断裂。
中文关键词: TC19钛合金  晶粒长大  激活能  拉伸性能
Abstract:The grain growth behavior in the β phase field and its effects on the tensile properties were investigated in a TC19 titanium alloy forging billet. The experimental results show that the growth behavior of the β grain can be effectively described by the Beck equation, and the grain growth kinetics exponents are found to be 0.517, 0.521, and 0.536 at 975 ℃, 990 ℃, and 1 005 ℃, respectively. Moreover, the apparent activation energy Q for grain growth is about 226.9 kJ/mol based on the Arrhenius relation.The tensile performance shows that the size of the β grain has little influence on room temperature strength in this work, the typical quasi-cleavage fracture morphology is dominant.
文章编号:     中图分类号:    文献标志码:
基金项目:
引用文本:


用微信扫一扫

用微信扫一扫